Core 2-Komponenten Wärmeleitkleber 5g

Core 2-component heat conducting adhesive

• Properties
  • The Alphacool 2-part thermal adhesive is electrically non-conductive. The high metallic content of aluminium nitride (70 - 73 %) guarantees optimal thermal conductivity. The thermal adhesive creates a stable adhesive bond. Due to the material composition, mechanical variances between the components to be bonded can also be compensated well. Surface curing is achieved after 2h (at 25°C ambient temperature). Complete curing takes place within 5 to 7 days (at 25°C ambient temperature).
• Application
  • All surfaces must be clean and free of grease, dust or contaminants. Important: The processing time is limited! As a rule, the processing time is about 10 minutes until the adhesive starts to cure. Adhesive (black) and applicator (yellow) must be thoroughly mixed in a ratio of 4:1 on a clean surface for approx. 2 to 3 minutes with a spatula. Perfect mixing is important to ensure an optimum bond. The two-part adhesive can then be applied thinly to the surfaces to be bonded using a spatula. Finally, the components to be bonded are pressed together. Higher ambient temperatures during processing ensure effective curing of the adhesive and increase strength at higher temperatures.

• Mixing ratio (adhesive : activator) 4 : 1
• Surface curing (at 25°C) 2 h
• Total curing (at 25°C) 5-7 Days
• Boiling point >200°C
• Flash point >88°C
• Specific gravity (yellow component) 0,97 g/cm3
• Specific gravity (black component) 2,08 g/cm3

• Aluminium nitride 70 - 73 %
• Epoxy resin 20 - 22 %
• Epoxy diluent 4 - 6 %
• Carbon black 0,5 - 1 %
• Substituted silane 0.1 - 0.2 %
• Total weight 4 g

• Polyamide 80 - 100 %
• Additive 0 - 5 %
• Total weight 1 g